5005A, TRANS, 75ML

Silicone adhesive sealant 5005A is a high modulus, one part acetoxy curing sealant conforming to ISO 11600. In its uncured state, the sealant is a thixotropic paste which can be applied over a wide range of temperatures with no risk of slumping from normal joint widths. The product cures rapidly on exposure to moist air to provide a resilient rubber seal capable of repeated extension and compression during service with excellent resistance to aging, shrinkage, cracking and discolouration. Silicone adhesive sealant 5005A offers good adhesion to various non-porous substrates such as glass, glazed ceramic tiles and Aluminium and is therefore recommended for producing formed-in-place gaskets, draught-proofing of windows and doors, on-site and factory-channel glazing of flat or profiled glass, patent glazing, curtain wall sealing and for ceramic and plastic joints in sanitary ware, laboratories and hospitals where ease of cleaning and a high standard of hygiene are essential.

• Non returnable 75ml cartridges
• Smooth easily extruded translucent paste
• 1.03 specific gravity
• 8 to 20minutes skin over time
• 3mm, 1 day. 5mm, 3days cure rate
• 18 shore A, minimum hardness based on a 3mm sheet cured at ambient conditions for 7 days
• 450%, minimum elongation at break based on a 3mm sheet cured at ambient conditions for 7 days
• Tensile strength of 1.55Mpa minimum based on a 3mm sheet cured at ambient conditions for 7 days
• Temperature resistance of -60°C to +204°C (Short term 218°C)
• Flash point greater than 100°C, burns at high temperatures to form an ash without dripping